Daler-Rowney Georgian Oil Color - Raw Sienna, 225 ml tube

Pigment Information

This color contains the following pigments:

PY42-Yellow Iron Oxide

PBk9-Ivory Black

PR101-Red Iron Oxide

Pigment Name

PY42-Yellow Iron Oxide

Chemical Name

iron(III)-oxide, hydrated

Chemical Formula

Fe2O3 • H2O

Properties

Yellow Ochre provides artists with earthtones from cream to brown. It has good hiding power, produces a quick drying paint, and can be safely mixed with other pigments. Its transparency varies widely from opaque shades to more transparent ones, which are valued for their use as glazes. If gypsum is present, Yellow Ochre is not suitable for frescoing. (See Brown Ochre, PY43.) PY42 is made from synthetic iron oxides. PY43 is made from natural iron oxide.

Permanence

Yellow Ochre has excellent permanence because ochres are some of the most permanent pigments available.

Toxicity

Yellow Ochre is non-toxic unless it contains manganese.

History

Ochre comes from the Greek word ochros, meaning pale yellow. It was one of the first pigments to be used by human beings, and evidence of its use has been found at 300,000 year old sites in France and the former Czechoslovakia.

Pigment Name

PBk9-Ivory Black

Pigment Type

charred animal bone

Chemical Name

carbon + calcium phosphate

Chemical Formula

C + Ca3(PO4)2 or C x CaPO4

Properties

Ivory Black is a cool, semi-transparent blue-black with a slight brownish undertone and average tinting strength. It mixes well with any color, and creates a range of dull greens when mixed with yellow. It has good properties for use in oil, can be slow to dry in oil form, and should never be used in underpainting or frescoing. Ivory Black is denser than Lamp Black.

Permanence

Ivory Black is very lightfast and has good permanence, though it is considered the least permanent of the major black pigments.

Toxicity

Ivory Black has no significant hazards.

History

Ivory Black is a carbon based black first named as Elephantium, and described in the 4th century BCE as produced by heating ivory scraps in clay pots to reduce the ivory or bone to charcoal. The deviation in names is because the more expensive varieties of this pigment were made by burning ivory, and the less expensive ones by burning animal bone. In the 19th century, the name Ivory Black was finally permitted to be applied to Carbon Black pigments made from bone. True Ivory Black is rare in modern times due to the protection of ivory, and the synthetic variety produced today was discovered in 1929. Bone Black is produced as an industrial pigment.

Pigment Name

PR101-Red Iron Oxide

Pigment Type

earth, synthetic

Chemical Name

iron oxides (synthetic), iron oxide, silica, alumina, lime, and magnesia or hydrated iron oxide

Chemical Formula

Fe2O2 or Fe2O3 x H2O

Properties

Red iron oxide varies in hue and transparency, depending on hydration and slight impurities. Indian Red is a slightly duller, deep brick hue with a bluish undertone. It is very dense and opaque, with excellent tinting strength and covering power. It is dependable when mixing with all other permanent pigments and yields good flesh tints when mixed with Zinc White. It is the synthetic version of PR102, which is a pigment made from earth reds, or natural red iron oxides, and the names applied to PR101 and PR102 often overlap. The synthetic red iron oxides have mostly replaced natural red iron oxides and are brighter, stronger, finer, and more permanent. Indian Red is the highest grade bluish shade. Light Red, English Red, and Venetian Red are yellowish shades. Mars Violet is a dull and subdued bluish or purplish oxide.

Permanence

Red iron oxide is very lightfast with excellent permanence.

Toxicity

Red iron oxide has no significant hazards.

History

Natural red iron oxide comes from the mineral ore hematite, called bloodstone by the ancient Greeks from the word hema, meaning blood. It is one of the oldest pigments, has been used by every major civilization, and was an important mineral for medieval alchemists. It was not widely used in artists' materials until the 17th century and was not produced in large quantities until the 18th century.